Structural and Optical Studies of Single-Crystal La_7/8Sr_1/8MnO₃
La_7/8Sr_1/8MnO₃の結晶構造と光学特性測定

The temperature- and field-dependent x-ray powder diffraction profiles of single-crystal La_7/8Sr_1/8MnO₃ show a sequence of structural phase transitions (O-O'-O''). The structurally nonuniform state was present in the certain intermediate temperature range. Moreover, the optical conductivity exhibits coexisting small polarons and a high-energy absorption band at ~ 12000 cm^-1 down to the low temperature, 30 K. All these results would constitute a clear indication of phase separation in La_7/8Sr_1/8MnO_3.

Dept. of Physics, National Taiwan Normal University: H. L. Liu, J. L. Her
Moscow Steel and Alloys Institute: Y. M. Mukovskii
IMR, Tohoku University: K. Koyama, K. Watanabe

La_7/8Sr_1/8MnO₃ について強磁場(5T)・低温(8.2-290 K)下のX線回折実験を行った．その結果，逐次構造相転移((O-O'-O'')を観測するとともに，その中間過程で結晶構造の不均一な状態が存在することが見出された．さらに，200Kにおける磁場効果は昇温と類似することも明らかとなった．一方，30Kにおける光学伝導度測定の結果は，小さなポーラロンと高エネルギー吸収バンド(~12000 cm^-1)の共存を示した．これらの結果は，La_7/8Sr_1/8MnO₃中に相分離状態が存在することを示している．

Dept. of Physics, National Taiwan Normal University: H. L. Liu, J. L. Her
Moscow Steel and Alloys Institute: Y. M. Mukovskii
東北大学金属材料研究所：小山佳一，渡辺和雄