Field-induced Structural Transformation in MnAs1-xSbx
MnAs1-xSbxの磁場誘起構造相転移
Structural transformation induced by magnetic fields on MnAs and MnAs0.9Sb0.1 was investigated by the X-ray diffraction measurements in high magnetic fields up to 5 T around room temperature. For MnAs, a single phase of the orthorhombic MnP-type structure was transformed into the hexagonal NiAs-type structgure by applying a magnetic field of 4 T in first-order. For MnAs0.9Sb0.1, the coexistence of field-induced ferromagnetic and paramagnetic crystal structures with different lattice parameters was confirmed 2.5 T.
IMR, Tohoku University: F. Ishikawa, K. Koyama, K. Watanabe
Fac. of Eng., Kyoto University: H. Wada, T. Asano
Reference: F. Ishikawa, K. Koyama, K. Watanabe, T. Asano and H. Wada, "Structural transformation of MnAs1-xSbx under high magnetic fields", Mater. Trans. 45 (2004) 311-314.
MnAsとMnAs0.9Sb0.1における磁場誘起の構造相転移について最大5 Tまでの磁場中で強磁場X線回折装置を用いて調査した．MnAsにおいては4 Tの磁場印加により常磁性の斜方晶MnP型結晶構造から六方晶NiAs型構造への一次での構造相転移が確認された．MnAs0.9Sb0.1においては2.5 Tの磁場中で，磁場誘起の強磁性と常磁性に対応した，異なる格子定数を持つ二種類の六方晶NiAs結晶構造が共存していることが確認された．
東北大学 金属材料研究所：石川文洋，小山佳一，渡辺和雄
京都大学 大学院工学研究科：和田裕文，浅野哲也